Negri D., Paoluzi A., Pareti L. Magnetic anisotropy and magnetisation processes in 3:29, 1:12 and 2:17 type Nd:(Fe, Co, Ti) related compounds. In: Journal of Magnetism and Magnetic Materials, vol. 269 (3) pp. 302 - 310. Elsevier, 2004.
A study of the composition and temperature dependence of the magnetocrystalline anisotropy has been performed in the pseudo-ternary system Nd3(Fe1 xCox)29 yTiy (x 0; 0.1, 0.3, 0.5, 0.7, 1.0 and y 1:5) and in the corresponding compositions 2:17and 1:12 related phases. The occurrence of field induced transitions, which were identified as firstorder magnetisation process, was observed in all the phases. In most of the samples the transitions still persist at room temperature. It has been found that the definition of easy and hard directions in the 3:29 phase results from the combined anisotropy contributions of the 1:12 and 2:17constituent blocks. The additivity of the anisotropy contributions is accomplished only qualitatively.
URL: http://www.sciencedirect.com/science/article/pii/S0304885303006188
DOI: 10.1016/S0304-8853(03)00618-8
Subject Permanent magnets materials
Magnetocrystalline anisotropy
Spin reorientation transitions
Rare earth

Icona documento 1) Download Document PDF

Icona documento Open access Icona documento Restricted Icona documento Private


Per ulteriori informazioni, contattare: Librarian http://puma.isti.cnr.it

Valid HTML 4.0 Transitional