Licci F., Turilli G., Ferro P., Ciccarone A. Low-temperature synthesis and properties of LaMnO3 +/- d and La0.67R0.33MnO3 +/- d (R = Ca, Sr, Ba) from citrate precursors. In: Journal of the American Ceramic Society, vol. 86 (3) pp. 413 - 419. American Ceramic Society, 2003.
 
 
Abstract
(English)
LaMn1-y3+Mny4+O3+/-d and La0.67R0.33Mn1-y3+Mny4+O3+/-d (R = Ca, Sr, Ba) phases were synthesized at 350degreesC by using very reactive, amorphous precursors obtained from the stoichiometric citrate solutions. The chemical process was optimized with respect to the solution concentration, pH, and additives. The precursor reactions were investigated as a function of the cation stoichiometry and the additive by simultaneous thermal and thermogravimetric analysis and X-ray diffraction. The reaction pathway was found to be independent of the cation stoichiometry, but related to the acid or base additive. The annealing temperature was systematically increased in the 350-1200degreesC interval and the La0.67Sr0.33MnO3+/-d properties (i.e., crystal sizes, Mn average valence, Curie temperature, magnetization, magnetic susceptibility) were measured and found to vary consistently as a function of it.
URL: http://www3.interscience.wiley.com/journal/118861435/abstract
DOI: 10.1111/j.1151-2916.2003.tb03314.x
Subject Giant Magnetoresistance; Transport properties; Defect structure; Phase-diagram; Doped LaMnO3; Perovskites; Mn; Nonstoichiometry; Magnetotrasport; Stoichiometry


Icona documento 1) Download Document PDF


Icona documento Open access Icona documento Restricted Icona documento Private

 


Per ulteriori informazioni, contattare: Librarian http://puma.isti.cnr.it

Valid HTML 4.0 Transitional